Lamina/tabula/panel polyethyleni ponderis molecularis altissimi
Detalia Producti:
LAMINA UHMWPELaminas UHMWPE varias secundum necessitates diversas cum applicatione diversa fabricare possumus. Ut resistentia UV, igni, antistatica, et cum aliis notis. Optima qualitas cum superficie et colore bono laminas nostras UHMWPE magis magisque populares toto orbe terrarum faciunt.
| Crassitudo | 10mm - 260mm |
| Magnitudo Standardis | 1000*2000mm, 1220*2440mm, 1240*4040mm, 1250*3050mm, 1525*3050mm, 2050*3030mm, 2000*6050mm |
| Densitas | 0.96 - 1 g/cm³ |
| Superficies | Levis et eminens (anti-lapsus) |
| Color | Natura, albus, niger, flavus, viridis, caeruleus, ruber, etc. |
| Officium Processus | Machinatio CNC, fresatura, formatio, fabricatio et compositio |
ProductumPerfunctio：
| Non. | Res | Unitas | Norma Probationis | Resultatum |
| 1 | Densitas | g/cm³ | GB/T1033-1966 | 0.95-1 |
| 2 | Contractio fingendi percentualis | ASTMD6474 | 1.0-1.5 | |
| 3 | Elongatio ad fracturam | % | GB/T1040-1992 | 238 |
| 4 | Robur tensile | MPA | GB/T1040-1992 | 45.3 |
| 5 | Examen duritiae indentationis globuli 30g | MPA | DINISO 2039-1 | 38 |
| 6 | Durities Rockwelliana | R | ISO868 | 57 |
| 7 | robur flexionis | MPA | GB/T9341-2000 | 23 |
| 8 | Robur compressionis | MPA | GB/T1041-1992 | 24 |
| 9 | Temperatura statica emollitionis | ENISO3146 | 132 | |
| 10 | Calor specificus | KJ (kg.K) | 2.05 | |
| 11 | Robur impactus | KJ/M3 | D-256 | 100-160 |
| 12 | conductivitas caloris | %(m/m) | ISO11358 | 0.16-0.14 |
| 13 | Proprietates labendi et coefficiens frictionis | PLASTICA/CHALYBUM (UMIDUM) | 0.19 | |
| 14 | Proprietates labendi et coefficiens frictionis | PLASTICA/CHALYB (SICCA) | 0.14 | |
| 15 | Duritia litoris D | 64 | ||
| 16 | Robur Impactus Incisum Charpy | mJ/mm² | Nulla pausa | |
| 17 | Absorptio aquae | Levis | ||
| 18 | Temperatura deflectionis caloris | °C | 85 |
Certificatum Producti：
Comparatio Efficaciae：
Alta resistentia abrasionis
| Materiae | UHMWPE | PTFE | Nylon 6 | Chalybs A | Polyvinylfluoridum | Chalybs purpureus |
| Frequentia Detritionis | 0.32 | 1.72 | 3.30 | 7.36 | 9.63 | 13.12 |
Bonae proprietates autolubricantes, frictio humilis
| Materiae | UHMWPE -carbo | Lapis fusus-carbo | Acu Pictacarbo laminaris | Non acu picta lamina-carbo | Carbo concretus |
| Frequentia Detritionis | 0.15-0.25 | 0.30-0.45 | 0.45-0.58 | 0.30-0.40 | 0.60-0.70 |
Alta vis impacti, bona tenacitas
| Materiae | UHMWPE | Lapis fusus | PAE6 | POM | F4 | A3 | 45# |
| Impactusrobur | 100-160 | 1.6-15 | VI-XI | 8.13 | 16 | 300-400 | DCC |
Involucrum Producti:
Applicatio Producti:
1. Tegumentum: Silos, infundibula, laminae resistentes attritioni, brachia, instrumenta refluxus similia canaliculi, superficies labens, cylindrus, etc.
2. Machinae Cibariae: Claustra, rotae stellatae, rotae ductoriae, rotae volubiles, tegulae tegumentorum ferentium, etc.
3. Machina chartae faciendae: Lamina operculi aquarii, lamina deflectoris, lamina tergiculi, alae aquariae.
4. Industria chemica: Laminam impletionis obsigna, materiam densam imple, capsas formae vacui, partes antliae, tegulas tegumentorum ferentium, rotas dentatas, superficiem iuncturae obsigna.
5. Alia: Machinae agriculturae, partes navium, industria galvanoplastica, partes mechanicae temperaturae infimae.