Pepa PE extruded kiʻekiʻe
Waiwai
● ʻOkoʻa waiwai no ka PE 1000
● ʻAʻahu maikaʻi a me ka pale ʻana i ka abrasion
● ʻAno maikaʻi ka leo dampening
● Pono ka meaʻai
Nā noi
● Nā papa ʻoki
● Hutes Liners
● Hoʻoponopono meaʻai
● ʻāpana kaulahao
ʻIkepili kino:
| 'ikamu | Pepa HDPE (Polyethylene). |
| ʻAno | extruded |
| mānoanoa | 0.5---200mm |
| Nui | (1000-1500)x(1000-3000)mm |
| kalakala | Keʻokeʻo / ʻeleʻele / ʻōmaʻomaʻo / melemele / uliuli |
| Pākuʻi | 0.96g/cm³ |
| Kūleʻa wela (hoʻomau) | 90 ℃ |
| Kūleʻa wela (ka wā pōkole) | 110 |
| Lae hehee | 120 ℃ |
| Ke aniani hoʻololi wela | _ |
| Linear thermal expansion coefficient | 155×10-6m/(mk) |
| (ka awelika 23~100 ℃) | |
| Awelika 23--150 ℃ | |
| Hiki ke ʻā (UI94) | HB |
| Tensile modulus o ka elasticity | 900MPa |
| E komo i loko o ka wai ma 23 ℃ no 24h | _ |
| Hoʻokomo i loko o ka wai ma 23 ℃ | 0.01 |
| ʻO ke koʻikoʻi hoʻopaʻapaʻa e kūlou ana/ ʻO ke koʻikoʻi uʻi mai ka haʻalulu | 30/-Mpa |
| ʻO ka uhaki ʻana i ka tensile | _ |
| ʻO ke koʻikoʻi koʻikoʻi o ke kaumaha maʻamau-1%/2% | 3/-MPa |
| ʻO ka hoʻāʻo ʻana i ka hopena o ka pendulum gap impact | _ |
| ʻO ka pānaʻi ʻana | 0.3 |
| ʻO Rockwell paʻakikī | 62 |
| Ka ikaika dielectric | >50 |
| Kūleʻa leo | ≥10 15Ω×cm |
| Kūʻē ʻili | ≥10 16Ω |
| Paʻa dielectric pili-100HZ/1MHz | 2.4/- |
| Helu helu hoʻopaʻa koʻikoʻi (CTI) | _ |
| Hiki ke hoʻopaʻa | 0 |
| Pili meaʻai | + |
| Kūʻai ʻakika | + |
| Kūʻē alkali | + |
| Kūleʻa wai kalapona | + |
| Ke kūʻē ʻana o ka hui ʻala | 0 |
| Kūʻē Ketone | + |